Effect of Mixing Time in Fly Ash Block Property
Effect of mixing time on fly ash block property
Ayan Kumar Keora a a

Development Alternatives, B-32, TARA Crescent, Qutab Institutional Area, New Delhi – 110016, India Abstract: This paper presents the effects of mixing time on the compressive strength of fly ash brick. Before designing the mix, sieve analysis of sand and fly ash was carried out and their fineness moduli were determined. Also the specific gravity and calorific value and ash content of fly ash were determined. The CaO content of lime also was determined by lime testing kit. The material batching is based on the composition derived from TARA laboratory report. Composition Sand Flay ash Virgin lime Phosphogypsum

50 50 9% of the total weight of sand and fly ash 3% of the total weight of sand and fly ash

The mixing duration was varying 6 minutes to 30 minutes. The strengths were measured at the curing ages of 28 days using compressive strength machine. The results revealed that the compressive strengths of fly ash bricks appreciably increased with increase in mixing duration from 6 minutes to 15 minutes but remained almost constant beyond 12 minutes for 28 days ages tested. For example, at 6, 8, 10, and 12 minutes mixing; the compressive strengths at 28 days 2 were 147.15, 149.59, 158.54, and 197.72 kg/cm respectively while at 14, 15, 20, 25 and 30 minutes mixing ; the compressive strengths at 28 days were 212.83, 2 216.54, 216.59, 221.34 and 227.12 kg/cm .

Keywords: Compressive strength, curing, machine mixing, mixing duration

Introduction Modern Construction prefers use of fly ash bricks. This one of the global go-green initiatives, and we are an active member of the same. This noble cause is supported by manufacturing and supplying bricks made from re-usable fly ash. Fly-Ash Bricks are an environment friendly cost saving building product. These bricks are 3 times stronger than conventional bricks with consistent strength. These bricks are ideally suited for internal, external, load

You May Also Find These Documents Helpful

  • Good Essays

    The study aims to investigate and compare commercial bricks to bricks made from Coconut fiber in terms of: hardness, durability, and cost.…

    • 856 Words
    • 4 Pages
    Good Essays
  • Good Essays

    Separation of Mixtures

    • 591 Words
    • 3 Pages

    * Introduction: A compound is a pure chemical substance consisting of two or more different chemical elements that can be separated into simpler substances by chemical reactions. Unlike a compound, a mixture is a material system made up by two or more different substances which are mixed together but are not combined chemically. There are two kinds of mixtures, homogeneous and heterogeneous. Homogeneous mixtures have the same composition and appearance throughout, while heterogeneous mixtures consist of visibly different parts. The purpose of this experiment is to create and separate a heterogeneous mixture consisting of sawdust, sand, beads, salt, and water. The hypothesis of this experiment is that the materials can be separated back into their original forms with the same masses.…

    • 591 Words
    • 3 Pages
    Good Essays
  • Satisfactory Essays

    Panera Case Study

    • 183 Words
    • 1 Page

    Table 3 shows the flow value of the mixtures containing BA. It shows that flow value for the BA blended cement mortars were decreased with increase in the percentage of BA. The control mix (BAM 0) has a flow value of 147 mm [30]. The flow value of mixes BAM 5, BAM 10, BAM 15, BAM 20, BAM 25, and BAM 30 shows decrease of 146, 146, 145, 144, 143, and 142 mm respectively. BA requires more water for proper consistency when compared to that of ordinary Portland cement due to irregular shape with rough surfaces, high porous texture and absorptive in nature [5]. Increase in water demand of BA, decreases the flow value and resulted in poor workability. W/C ratio was kept same as 0.5 for all mixes. The flow value of BAM 30 reduced to 3.4 % due to…

    • 183 Words
    • 1 Page
    Satisfactory Essays
  • Good Essays

    Roman Pozzolanic Concrete

    • 680 Words
    • 3 Pages

    Concrete is a mixture made up of an aggregate, a binding agent and water. Typically the aggregate is gravel, sand or small stones. This is the filler that gives the final product its mass. The binding agent is what causes the mixture to set and harden. When the aggregate and binding agent are combined with water a thick mixture is created that can be poured into a form which then solidifies. In early civilization the binding agent was typically limestone powder or gypsum. The Romans discovered the use of pozzolana as a binding agent (Yegeul, n.d.). Pozzolana is a fine, sandy, volcanic ash which when used as a binding agent creates a strong durable concrete (Wikipedia, 2011, Pozzolana).…

    • 680 Words
    • 3 Pages
    Good Essays
  • Good Essays

    Hollow blocks are one of the most used building materials in our time. Since hollow blocks weigh around 9-11 kg, it is a must for reinforcement steel to be placed into the gaps of the hollow blocks and/or to be built on a strong foundation in order to avoid settling or cracking. A higher capital is needed for a strong foundation that can hold the weight of standard concrete hollow blocks (esp. for high and large buildings). The heavier the hollow blocks, the greater the force exerted to lift them. This may lead to problems like back pains, abrasions, muscle pains and the like. Therefore, hollow blocks must be lighter. Light aggregates must be used like lahar, carbonized rice hull and rice hull ash.…

    • 6973 Words
    • 28 Pages
    Good Essays
  • Powerful Essays

    Brick is a masonry unit of clay, formed into a rectangular prism while plastic and hardened by firing in a kiln. The manufacture of bricks is used easily workable and clayey materials and the materials are avoided to contain any large hard components or lumps of lime, this is to avoid crack and split of the brick. We can obtain clay on the surface of the ground. There are three principal form of clay used to manufactured clay brick which are surface clay, shales, and fire clays. The surface clays is…

    • 1651 Words
    • 7 Pages
    Powerful Essays
  • Powerful Essays

    A concrete mix was designed based on the BRE Manual Design of concrete mixtures. Then, a total of 40kg of the required proportions of Ordinary Portland cement which includes water, fine aggregate, and 20mm size crushed gravel coarse aggregate was weighed out. The materials are then batched and mixed in a pan mixer. Next, a slump test for the concrete mixture was carried out. The concrete mixture was then used to produce 4 no. 100mm cubes and two 500 x 100 x 100 mm prisms based on table 1.1. Finally, the specimens were labeled and covered for curing. Sieving was also conducted on the fine and course aggregate to produce a sieving analysis chart.…

    • 1463 Words
    • 6 Pages
    Powerful Essays
  • Best Essays

    Waste Minimization

    • 3158 Words
    • 13 Pages

    The material waste is the main source in construction activity because most of the raw materials from which construction inputs are derived come from non-renewable resources. The term “waste” is a familiar term in the industry all over the world. The various sources of waste are…

    • 3158 Words
    • 13 Pages
    Best Essays
  • Powerful Essays

    Hypo Sludge

    • 9262 Words
    • 38 Pages

    DETERMINATION OF COMPRESSIVE STRENGTH 44 DETERMINATION OF FLEXURAL STRENGTH 45 STATISTICAL TREATMENT 45 FLOW OF THE EXPERIMENTAL STUDY 47 LIST OF TABLES TABLE No. | TITLE | 1 | Classes of Aggregates | 2 | Composition of Portland cement with chemical composition and weight percentage | 3 | A table of admixtures and their functions | 4 | Properties of Raw Hypo Sludge | 5 | Properties of Hypo Sludge as Cement Ingredient | 6 | Comparison of Cement and Hypo Sludge | 7 | Number of Specimens Tested for Compression | 8 | Number of Test Specimens for Flexural Strength Test At 14 Days Curing Period | LIST OF FIGURES FIGURE No. | TITLE | 1 | Conceptual Paradigm of the Study | 2 | A flow diagram of Portland cement production | 3 | Schematic diagram of rotary kiln | 4 | Schematic illustration of the pores in calcium silicate through different stages of hydration | 5 | Rate of heat evolution during the hydration of Portland cement | 6 | Schematic drawings to demonstrate the relationship between the…

    • 9262 Words
    • 38 Pages
    Powerful Essays
  • Better Essays

    GEOTECHNICAL INSTRUMENTATION

    • 3765 Words
    • 16 Pages

    Single-component bentonite grouts have been used in related industries a long time, and have been adopted for borehole instrumentation…

    • 3765 Words
    • 16 Pages
    Better Essays
  • Powerful Essays

    Setting Time of Cement Lab

    • 1624 Words
    • 7 Pages

    This report is a part of CVE 335 Cement and Concrete Materials Laboratory for civil engineering junior students. This project is about the normal consistency and the setting time of cement paste. The data on this individual report is based on our experiment which my group and I have done last Thursday.…

    • 1624 Words
    • 7 Pages
    Powerful Essays
  • Good Essays

    In the comparative study of influence of the aggregate on high strength concrete, here is an attempt to study strength characteristics of cubes and cylinders comprising of combination of different size of coarse aggregates namely 20MM,10MM and crushed sand. The experimental analysis has been divided into two categories by comparing the quality of concrete produced by not using 20mm in the mix design to form the compact and better flow in concrete against using standard grading techniques. The concrete mix design for characteristics M40, M50 strength, the water cement ratio is kept variable as regards to workability are accessed, The strength parameters of hardened concrete like compressive strength, split test strength are observed.…

    • 1329 Words
    • 5 Pages
    Good Essays
  • Better Essays

    Fresh concrete is a homogenous mixture of water, cement, aggregates (coarse and fine), air and in some cases admixtures may be used. Admixture is used in certain cases to control rheology, rate of setting, hardening and durability. After mixing the constituent materials to produce a uniform blend, operations such as transporting, compacting, placing and the finishing of fresh concrete can all affect the properties of hardened concrete. It is important that the constituent materials remain s uniformly distributed within the concrete mass during the various stages of its handling and also that full compaction is achieved. Whenever these conditions are not…

    • 1166 Words
    • 5 Pages
    Better Essays
  • Powerful Essays

    Brick making is indispensable for the economy of Bangladesh. Though not formally recognized as an industry, brick-making is a significant economic activity in Bangladesh. The country’s overwhelming dependence on bricks is due to its lack of stones in any sizable quantity or other alternative building materials at comparable cost.…

    • 3536 Words
    • 15 Pages
    Powerful Essays
  • Good Essays

    India is witnessing construction of very interesting projects in all sectors of Infrastructure. High rise structures, under construction, include residential/commercial blocks up to a height of 320 m and RC chimneys for thermal power stations extending upwards up to 275m. Majority of the structures are in structural concrete. The functional demands of such high rise structures include the use of durable materials. High Strength Concrete, Self–compacting Concrete are gaining widespread acceptance. Apart from the basic structural materials, modern projects require a variety of secondary materials for a variety of purposes such as construction chemicals, waterproofing materials, durability aids etc. The paper highlights some of the recent developments.…

    • 1769 Words
    • 8 Pages
    Good Essays